Current location: Home > Products > Coating Additives
Product Details
|
Name
|
Product Name
|
Simila
Product
|
Application
System
|
Content
|
Product Features
|
|
Titanate
coupling agent
|
MOL-101
|
KR-TTS
|
S
|
100%
|
Improve the compatibility of inorganic filler and resin, reduce the system viscosity, improve the filling amount of inorganic filler, improve the dispersion of magnetic powder on the substrate and the adhesion to the polymer.
|
|
Titanate
coupling agent
|
MOL-102
|
KR-TTS
|
S
|
100%
|
Reduce the drying temperature, baking time, the pigment dispersion, and prevent sinking.
|
|
Titanate
coupling agent
|
MOL-105/F105
|
KR-TTS
|
S
|
90%
|
The packing is easier to disperse, reduce the system viscosity, improve the packing amount to reduce the cost, the coating has better smoothness, the film has good wear resistance and resistance to corrosion. It is widely used in magnetic coatings and anticorrosive coatings.
|
|
Titanate
coupling agent
|
MOL-70
|
KR-TTS
|
S
|
100%
|
The product has no smell and is a good dispersant for the face and filler.
|
|
Titanate
coupling agent
|
MOL-9SA
|
KR-9S
|
S
|
100%
|
Suitable for high temperature mixing processing to reach the packing is more easily dispersed, reduce the system viscosity, improve the packing capacity, reduce the cost, can also be used as a touch change agent.
|
|
Titanate
coupling agent
|
MOL-22
|
TTOP-12
|
S
|
90%
|
Light color, filler is easier to disperse, reduce system viscosity, better cover force, reduce cost, coating has better smoothness, settlement prevention, film formation has good wear resistance and corrosion resistance.
|
|
Titanate
coupling agent
|
MOL-144
|
KR-38S
|
S
|
90%
|
It is better than MOL-22, the filler is more dispersed, and suitable for surface treatment of calcium carbonate and various silates.
|
|
Titanate
coupling agent
|
MOL-311
|
KR-238S
|
S
|
85%
|
Better dispersion, anti-settlement, can increase the amount of packing in the coating, can increase the coating waterproof, fire prevention, anti-corrosion ability, conductive coating is widely used.
|
|
Titanate
coupling agent
|
MOL-311WA
|
KR-238T
|
S/W
|
100%
|
It is still stable in the aqueous environment, which can improve the pigment dispersion and film formation physical properties.
|
|
Titanate
coupling agent
|
MOL-311W
|
KR-238T
|
W
|
60%
|
Suitable for water-based coatings, can improve the pigment dispersion, film-forming physical properties.
|
|
Titanate
coupling agent
|
MOL-401
|
KR-41B
|
S/W
|
50%
|
Better dispersion, anti-settlement, can increase the amount of packing in the coating, improve the impact strength of the coating, unsaturated polyester glass is widely used.
|
|
Titanate
coupling agent
|
MOL-126
|
KR-138S
|
S/W
|
50%
|
It is still stable in the aqueous environment, which can improve the pigment dispersion and film formation physical properties.
|
|
Titanate
coupling agent
|
MOL-4
|
TILCOMTET
|
S/W
|
60%
|
Dispersant of waterborne paint, crosslink of polyester paint.
|
|
Titanate
coupling agent
|
MOL-27
|
KR-TTS
|
S
|
95%
|
It is an excellent surface treatment agent for carbon black and other pigment and fillers. Good viscosity reduction effect, anti-sink, anti-floating color and hair flowers.
|
|
Titanate
coupling agent
|
MOL-120/121
|
|
S
|
100%
|
Suitable for unsaturated polyester / epoxy powder coating, high filling capacity, reduce viscosity, easier to disperse.
|
|
Name
|
Product Name
|
Similar
Product
|
Application
System
|
Content
|
Product Features
|
|
Titanate
coupling agent
|
MOL-119
|
|
S
|
100%
|
Suitable for unsaturated polyester / epoxy powder coating, cost-effective, reduce the viscosity, improve the filling amount.
|
|
Aluminate
coupling agent
|
MOL-B
|
|
S
|
100%
|
Aluminum-containing polymer, light, heavy calcium carbonate surface treatment, is the preferred dispersant for filling the base material.
|
|
Aluminate
coupling agent
|
MOL-B-1
|
|
S
|
90%
|
It is a liquid aluminate ester coupling agent, reducing viscosity, easier to disperse, suitable for inorganic mineral filling coating.
|
|
Borate coupling
agent
|
MOL-100P
|
|
S
|
100%
|
Boron-containing element has excellent chemical modification on inorganic filler surface and good luster.
|
|
Aluminum-titani
um composite
coupling Agent
|
MOL
|
|
S
|
100%
|
Including aluminum, titanium element polymer, suitable for all kinds of powder surface treatment.
|
|
Organic silicon
coupling agent
|
MOL-1018
|
|
S
|
100%
|
It has a strong surface treatment ability for calcium carbonate, and the treated calcium carbonate filled to PVC and PP can improve the mechanical properties.
|
|
Silane coupling
agent
|
MOL-550
|
A1100
|
S
|
100%
|
This product is an excellent glass fiber treatment agent to improve the mechanical strength, electrical properties and anti-aging properties of composite materials.
|
|
Silane coupling
agent
|
MOL-560
|
A-187/Z-6040
/KBM-403
|
S
|
100%
|
It is used in inorganic filler filling to enhance the composite materials and improve the mechanical strength, water resistance, heat resistance and other properties of the composite materials.
|
|
Silane coupling
agent
|
MOL-570
|
A-174/KBM-50
3/SH-6030
|
S
|
100%
|
Improving the bonding properties of organic and inorganic materials can also improve the physical properties of composite materials.
|